product list
- High Alumina Bricks
- Refractory Bricks
- Corundum Plastic Materials
- Refractory Castable
- High Aluminum Refractory Castable
- Light Refractory Castable
- Molten Copper Refractory Castable
- Silica Ramming Mass
- Silicon Carbide Refractory Castable
- Magnesite Basic Ramming Mass
- Refractory molded brick
- Corundum refractory Concrete
- Refractory precast block
- Zirconium refractory Mixture
- Magnesia refractory cement
- Silica Refractory Cement
- Refractory cement
- Fire clay
- Alumina Composite refractory concrete
- Refractory mortar
- Continuous casting Refractory cement
- Silica sand
- Quartz sand for copper smelting
- Molten Copper Refractory Material
- Molten copper ramming mass
- Molten copper refractory castable
- Acid induction furnace lining refractory cenent
- Castable Refractory for natural copper smelting
- Castable refractory furnace lining
- Application of refractory ramming mass
- Refractory materials furnace lining
- Amorphous Refractory Castable
- Molten Zinc Refractory Castable
- Molten Zinc Ramming Mass
- Molten Aluminum Refractory Material
- Ladle Castable
- Special Refractory Ramming Mass
- Accessory Material Refractory (Crystallizer)
- Silica Ramming Mass (GDL)
- Silica Ramming Mass (GYDL)
- Heavy Accessory Refractory Material
- High Strength Refractory Mortar
- Special Ramming Mass
- Light-weight Castable Refractory
- Castable Refractory
- Accessory Refractory Material
- High Grade Composite Silica Ramming Mass
- Corundum Plastic Refractory Cement
- Alumina Composite Ramming Mass
- Silica Refractory Ramming Mass
General specification for construction of refractory concrete
Environmental requirements of refractory concrete construction site
Construction site level.There is no sand, lime, clinker, slag and other sundries in the construction site.TNormal construction environment temperature at 5 ~ 40 ℃. construction water pH value is better in E. 6.5~7.5 storage and treatment of water equipment should be clean without debris.
Temperature control measures
When the temperature is higher than 40 DEG C, the shading treatment should be adopted when the B. temperature is below the temperature of 5 ℃:With 40 ℃ or so of hot water mixing refractory castable (in the first phase to ensure that the refractory material to adjust the temperature of hot water);A high power lamp or a similar heat source is used to maintain the temperature during the initial setting of the refractory material until the refractory has been hardened (at least 24 hours) and the temperature can be reduced.
Check before installation
Check the observation hole, temperature hole, pressure hole, etc. are arranged in place welding.Check the overall dimensions of the metal frame。Check the installation of the supporting plate and the reinforcing plate.The cylinder of the rotary kiln, the backiron, inspected the installation of retaining ring.
Installation of anchor
Make clear the type, material, layout, layout, welding requirements and technical requirements of the anchors to be used.On the use of the types of welding electrodes.Single anchor should be full welding.Combination anchor base should be full welding, V type nails and the base spot welding in order to shake when the separation is not good.
Welding of anchor
The anchor nail and the wall of the device should be fully welded and vertical to the wall.Y type anchor nails should be welded on both sides of the width.The weld surface shall not have undercut, porosity, slag, arc pit, incomplete fusion and leakage defects such as welding, and no residual slag and spatter.When the anchor is directly welded on the wall of the device, it should be close to the wall, and the gap should not be more than 1 mm.The welding quality inspection at least anchor of 1/20 hammer (0.5 kg) test to check the welding.In addition, the first and 500th anchors shall be subjected to impact bending test. If there is a suspected defect, the number of checks should be increased.
Construction of calcium silicate board
Preparation and use of binder
Binder for calcium silicate board supporting products, at the same time with thermal insulation and bonding function. Binder divided into bonded powders (bags) and adhesive liquid (barrels) two parts, supporting the use of. When mixing the two with mud binder.With the proportion of:Adhesive powder: binder liquid =1:3 (weight ratio).Should be used in accordance with the proportion of mixing mud mixing mud binder, the use and storage time should not exceed one hour.
Paste of calcium silicate board
Clean the surface of the construction site.Use wooden hammer or rubber hammer.Paste calcium silicate board should be pressure seam, wrong seam paste.
Taurus Refractory ramming mass Factory mainly engaged in professional manufacturer of development, production and sales of the refractory mixture such as melting copper, aluminum and zinc furnace lining. And supply castable refractory for copper smelting, ramming mass for molten copper,fire clay,refractory mortar, refractory cement ,refractory mixture, refractory concrete and silica sand for copper smelting.
Website: http://www.jnrefractory.com
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
Email: info@jnrefractory.com
gyjinniu@163.com
products list : castable refractory cement for up lead copper rod Molten Zinc Refractory Casting Molten Zinc Ramming Mass Molten Aluminum Refractory Material refractory castable for up lead copper rod Special Refractory Ramming Mass Copper alloy refractory materials for electric furnace acidic refractory for electric furnace body electric furnace refractory material for copper smelting Corrosion resistance Molen Zinc Refractory Castable for up lead copper rod High Strength Refractory Mortar Refractory installation services Fireclay Light-weight Castable Refractory Casting Refractory Accessory Refractory Material Corrosion resistance Quartz sand High Grade Composite Silica Ramming Mass Corundum Plastic Refrctory Alumina Composite Ramming Mass for horizontal continuous casting Silica Refractory Ramming Mass for horizontal continuou casting quartz sand refractory for copper smelting silica sand refractory for core induction furnace refractory concrete block pre-cast refractory block refractory ramming mixture fire clay for up lead copper rod refractory mortar for non core induction furnace refractory cement for copper smelting high grade composite silica mortar silica refractory cement Magnesia refractory cement
Environmental requirements of refractory concrete construction site
Construction site level.There is no sand, lime, clinker, slag and other sundries in the construction site.TNormal construction environment temperature at 5 ~ 40 ℃. construction water pH value is better in E. 6.5~7.5 storage and treatment of water equipment should be clean without debris.
Temperature control measures
When the temperature is higher than 40 DEG C, the shading treatment should be adopted when the B. temperature is below the temperature of 5 ℃:With 40 ℃ or so of hot water mixing refractory castable (in the first phase to ensure that the refractory material to adjust the temperature of hot water);A high power lamp or a similar heat source is used to maintain the temperature during the initial setting of the refractory material until the refractory has been hardened (at least 24 hours) and the temperature can be reduced.
Check before installation
Check the observation hole, temperature hole, pressure hole, etc. are arranged in place welding.Check the overall dimensions of the metal frame。Check the installation of the supporting plate and the reinforcing plate.The cylinder of the rotary kiln, the backiron, inspected the installation of retaining ring.
Installation of anchor
Make clear the type, material, layout, layout, welding requirements and technical requirements of the anchors to be used.On the use of the types of welding electrodes.Single anchor should be full welding.Combination anchor base should be full welding, V type nails and the base spot welding in order to shake when the separation is not good.
Welding of anchor
The anchor nail and the wall of the device should be fully welded and vertical to the wall.Y type anchor nails should be welded on both sides of the width.The weld surface shall not have undercut, porosity, slag, arc pit, incomplete fusion and leakage defects such as welding, and no residual slag and spatter.When the anchor is directly welded on the wall of the device, it should be close to the wall, and the gap should not be more than 1 mm.The welding quality inspection at least anchor of 1/20 hammer (0.5 kg) test to check the welding.In addition, the first and 500th anchors shall be subjected to impact bending test. If there is a suspected defect, the number of checks should be increased.
Construction of calcium silicate board
Preparation and use of binder
Binder for calcium silicate board supporting products, at the same time with thermal insulation and bonding function. Binder divided into bonded powders (bags) and adhesive liquid (barrels) two parts, supporting the use of. When mixing the two with mud binder.With the proportion of:Adhesive powder: binder liquid =1:3 (weight ratio).Should be used in accordance with the proportion of mixing mud mixing mud binder, the use and storage time should not exceed one hour.
Paste of calcium silicate board
Clean the surface of the construction site.Use wooden hammer or rubber hammer.Paste calcium silicate board should be pressure seam, wrong seam paste.
Taurus Refractory ramming mass Factory mainly engaged in professional manufacturer of development, production and sales of the refractory mixture such as melting copper, aluminum and zinc furnace lining. And supply castable refractory for copper smelting, ramming mass for molten copper,fire clay,refractory mortar, refractory cement ,refractory mixture, refractory concrete and silica sand for copper smelting.
Website: http://www.jnrefractory.com
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
Email: info@jnrefractory.com
gyjinniu@163.com
products list : castable refractory cement for up lead copper rod Molten Zinc Refractory Casting Molten Zinc Ramming Mass Molten Aluminum Refractory Material refractory castable for up lead copper rod Special Refractory Ramming Mass Copper alloy refractory materials for electric furnace acidic refractory for electric furnace body electric furnace refractory material for copper smelting Corrosion resistance Molen Zinc Refractory Castable for up lead copper rod High Strength Refractory Mortar Refractory installation services Fireclay Light-weight Castable Refractory Casting Refractory Accessory Refractory Material Corrosion resistance Quartz sand High Grade Composite Silica Ramming Mass Corundum Plastic Refrctory Alumina Composite Ramming Mass for horizontal continuous casting Silica Refractory Ramming Mass for horizontal continuou casting quartz sand refractory for copper smelting silica sand refractory for core induction furnace refractory concrete block pre-cast refractory block refractory ramming mixture fire clay for up lead copper rod refractory mortar for non core induction furnace refractory cement for copper smelting high grade composite silica mortar silica refractory cement Magnesia refractory cement