product list
- Refractory Bricks
- Corundum Plastic Materials
- Refractory Castable
- High Aluminum Refractory Castable
- Light Refractory Castable
- Molten Copper Refractory Castable
- Silica Ramming Mass
- Silicon Carbide Refractory Castable
- Magnesite Basic Ramming Mass
- Refractory molded brick
- Corundum refractory Concrete
- Refractory precast block
- Zirconium refractory Mixture
- Magnesia refractory cement
- Silica Refractory Cement
- Refractory cement
- Fire clay
- Alumina Composite refractory concrete
- Refractory mortar
- Continuous casting Refractory cement
- Silica sand
- Quartz sand for copper smelting
- Molten Copper Refractory Material
- Molten copper ramming mass
- Molten copper refractory castable
- Acid induction furnace lining refractory cenent
- Castable Refractory for natural copper smelting
- Castable refractory furnace lining
- Application of refractory ramming mass
- Refractory materials furnace lining
- Amorphous Refractory Castable
- Molten Zinc Refractory Castable
- Molten Zinc Ramming Mass
- Molten Aluminum Refractory Material
- Ladle Castable
- Special Refractory Ramming Mass
- Accessory Material Refractory (Crystallizer)
- Silica Ramming Mass (GDL)
- Silica Ramming Mass (GYDL)
- Heavy Accessory Refractory Material
- High Strength Refractory Mortar
- Special Ramming Mass
- Light-weight Castable Refractory
- Castable Refractory
- Accessory Refractory Material
- High Grade Composite Silica Ramming Mass
- Corundum Plastic Refractory Cement
- Alumina Composite Ramming Mass
- Silica Refractory Ramming Mass
Corundum Refractory Concrete
Model
| Properey | GS—70 | GS—75 | GS—80 | GS—85 | |
| Chemical composition(%) | Al2O3≥ | 70 | 75 | 80 | 85 |
| Cold crushing strength(MPa) |
110℃×24h After drying at |
10 | 12 | 15 | 15 |
|
600℃×3h After firing at |
16 | 20 | 20 | 22 | |
|
1200℃×3h After firing at |
25 | 25 | 26 | 28 | |
| Refractoriness under load (℃) | -0.2% | 1380 | 1400 | 1450 | 1500 |
| -0.4% | 1500 | 1550 | 1550 | 1580 | |
| Linear changing after burnt (%) |
1400℃×3h After firing at |
±2 | ±2 | ±1.5 | ±1.5 |
| Bulk density (g./cm3) |
1400℃×3h After firing at |
2.6 | 2.65 | 2.7 | 2.8 |
| Refractoriness≥ (℃) | 1700 | 1750 | 1790 | 1790 | |
| Amount for construction (kg/m3) | 2800 | 2850 | 2900 | 3000 | |
| Application | Induction smelting furnace for nonferrous metal and ferrous metal | ||||
| Characteristic |
T imeproof Corrosion resistance Thermal shock resistance Spalling resistance Volume stability High strength Abrasion resistance |
||||
Gongyi Taurus Refractory Material Factory is a professional refractory materials manufacturers and refractory materials suppliers,mainly supply Unshaped Refractories,Silicon Carbide Refractory Castable,Castable Refractory Cement,Pouring Material,Castable Refractory Concrete,Silica Ramming Mass etc. series of refractory materials products, sincerely welcome everyone to visit.
Website: http://www.jnrefractory.com
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
products list : castable refractory cement for up lead copper rod Molten Zinc Refractory Casting Molten Zinc Ramming Mass Molten Aluminum Refractory Material refractory castable for up lead copper rod Special Refractory Ramming Mass Copper alloy refractory materials for electric furnace acidic refractory for electric furnace body electric furnace refractory material for copper smelting Corrosion resistance Molen Zinc Refractory Castable for up lead copper rod