Ramming mass/fire clay Lining baking process of extended service life of furnace

Add ramming mass/fire clay lining: firstly, should tie good lining ahead of the completion of the preparatory work needs to add iron and bread baking. For iron. Fill furnace. Don't add oily iron pin, iron beans, iron machinery. Because top furnace lining ramming mass/fire clay without sintering with oily. The ramming mass/fire clay is heated by high temperature will discharge a lot of smoke and ammonia. After high pressure will put a lot of pressure to smoke, ammonia lining, lining after discharged to the outside of the furnace lining. The time has been a long time will more than leave a lot of smoke.
Starting from the current 0.2 start: electric disc holding for 20 minutes 20 minutes.0.4.0.3 insulation insulation insulation for 20 minutes 20 minutes.0.5.0.6 holding for 40 minutes. In the future, to the normal melt. The molten iron of full furnace. Heating to 1500 degrees - 1650 degrees. Keep warm for 60 minutes. The end of baking.
Second, about the start of the cold furnace, in this process, we should pay attention to what the problem, starting from 10 0.2 minutes.0.3 minutes to 10 minutes.0.4 to 5 minutes.0.5 to stay 5 minutes.0.6 5 minutes, and then the normal operation.
Note: heat furnace stopping furnace shutdown. Finally a furnace to the temperature rise, hit the net around the mouth. The glaze furnace molten copper is poured into the furnace wall. After investigation. Part of the furnace body of black ramming mass/fire clay lining has become thinner. At the next blow to the attention of the site. With the good furnace cover plate the ramming lining gradually shortened.

Taurus Refractory ramming mass Factory mainly engaged in professional manufacturer of development, production and sales of the refractory mixture such as melting copper, aluminum and zinc furnace lining. And supply castable refractory for copper smelting, ramming mass for molten copper,fire clay,refractory mortar, refractory cement ,refractory mixture, refractory concrete and silica sand for copper smelting.
Website: http://www.jnrefractory.com  
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
Email: info@jnrefractory.com
          gyjinniu@163.com
products list : castable refractory cement for up lead copper rod  Molten Zinc Refractory castable     Molten Zinc Ramming Mass     Molten Aluminum Refractory Material      refractory castable for up lead copper rod    Special Refractory Ramming Mass     Copper alloy refractory materials for electric furnace      acidic refractory for electric furnace body   electric furnace refractory material for copper smelting     Corrosion resistance       Molen Zinc Refractory Castable for up lead copper rod    High Strength Refractory Mortar      Refractory mortar installation services Fireclay   Light-weight Castable Refractory    castable Refractory    Accessory Refractory Material   Corrosion resistance Quartz sand    High Grade Composite Silica Ramming Mass    Corundum Plastic Refractory     Alumina Composite Ramming Mass for horizontal continuous castable     Silica Refractory Ramming Mass for horizontal continuou castable    quartz sand refractory for copper smelting     silica sand refractory for core induction furnace      refractory concrete block      pre-cast refractory block      refractory ramming mixture     fire clay for up lead copper rod      refractory mortar for non core induction furnace    refractory cement for copper smelting      high grade composite silica mortar     silica refractory cement     Magnesia refractory cement