The Influence Factors of Refractory cement Material Mixing Degree

1. The powder particle shape of powder particles of different shapes, and the effect of mixing time are not the same, such as spherical particles in the friction is small, the relative velocity in the mixing process, it is easy to mix evenly; and angular shaped particles in friction, not easy to mix, compared with the former the mixing time is relatively long, some.refractory cement

2. Effects of structural characteristics of mixing equipment for material mixing quality by wet grinding machine mixing mud, uniform and compact, good plasticity, and biaxial mixer mixed mud quality is worse.refractory cement

3. Mixed the length of time in general, long mixing time, the mixture is more uniform. The mixing stage, uniformity increases quickly when mixing after a certain period of time, for another long time effect on the uniformity is not obvious. To join or multi species dispersion of the clay, the mixing time should be longer. Such as clay brick with wet mill mixing time is 4 lOmin, a brick material; 15min; magnesia brick material needs 20 - 25min. The mixing time is not too long, otherwise there will be the following: 1) the size composition are to be crushed again and change; 2) mud fever and the effect of moisture content, or because the mud is too hot, and will increase the compression molding elastic aftereffect and spallation occurs when.

4. Sequence of feeding sequence has great influence on the mixing, if the coarse powder is added at the same time, the fine powder is concentrated into small particle and "white material easy to appear".refractory cement

Taurus Refractory ramming mass Factory mainly engaged in professional manufacturer of development, production and sales of the refractory mixture such as melting copper, aluminum and zinc furnace lining. And supply castable refractory for copper smelting, ramming mass for molten copper,fire clay,refractory mortar, refractory cement ,refractory mixture, refractory concrete and silica sand for copper smelting.
Website: http://www.jnrefractory.com  
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
Email: info@jnrefractory.com
          gyjinniu@163.com
products list : castable refractory cement for up lead copper rod  Molten Zinc Refractory castable     Molten Zinc Ramming Mass     Molten Aluminum Refractory Material      refractory castable for up lead copper rod    Special Refractory Ramming Mass     Copper alloy refractory materials for electric furnace      acidic refractory for electric furnace body   electric furnace refractory material for copper smelting     Corrosion resistance       Molen Zinc Refractory Castable for up lead copper rod    High Strength Refractory Mortar      Refractory mortar installation services Fireclay   Light-weight Castable Refractory    castable Refractory    Accessory Refractory Material   Corrosion resistance Quartz sand    High Grade Composite Silica Ramming Mass    Corundum Plastic Refractory     Alumina Composite Ramming Mass for horizontal continuous castable     Silica Refractory Ramming Mass for horizontal continuou castable    quartz sand refractory for copper smelting     silica sand refractory for core induction furnace      refractory concrete block      pre-cast refractory block      refractory ramming mixture     fire clay for up lead copper rod      refractory mortar for non core induction furnace    refractory cement for copper smelting      high grade composite silica mortar     silica refractory cement     Magnesia refractory cement