product list
- High Alumina Bricks
- Refractory Bricks
- Corundum Plastic Materials
- Refractory Castable
- High Aluminum Refractory Castable
- Light Refractory Castable
- Molten Copper Refractory Castable
- Silica Ramming Mass
- Silicon Carbide Refractory Castable
- Magnesite Basic Ramming Mass
- Refractory molded brick
- Corundum refractory Concrete
- Refractory precast block
- Zirconium refractory Mixture
- Magnesia refractory cement
- Silica Refractory Cement
- Refractory cement
- Fire clay
- Alumina Composite refractory concrete
- Refractory mortar
- Continuous casting Refractory cement
- Silica sand
- Quartz sand for copper smelting
- Molten Copper Refractory Material
- Molten copper ramming mass
- Molten copper refractory castable
- Acid induction furnace lining refractory cenent
- Castable Refractory for natural copper smelting
- Castable refractory furnace lining
- Application of refractory ramming mass
- Refractory materials furnace lining
- Amorphous Refractory Castable
- Molten Zinc Refractory Castable
- Molten Zinc Ramming Mass
- Molten Aluminum Refractory Material
- Ladle Castable
- Special Refractory Ramming Mass
- Accessory Material Refractory (Crystallizer)
- Silica Ramming Mass (GDL)
- Silica Ramming Mass (GYDL)
- Heavy Accessory Refractory Material
- High Strength Refractory Mortar
- Special Ramming Mass
- Light-weight Castable Refractory
- Castable Refractory
- Accessory Refractory Material
- High Grade Composite Silica Ramming Mass
- Corundum Plastic Refractory Cement
- Alumina Composite Ramming Mass
- Silica Refractory Ramming Mass
Zircon refractory cement for intermediate frequency
Zircon refractory cement for intermediate frequency of composition (mass%) was ZrO2 62, SiO2 32, Al2O3 2, Fe2O3 0.5, Bulk density is greater than 3g/cm3,The fire resistance is about 1790, Maximum particle size 0.5mm.Zircon refractory cement binding agent for phosphate two aluminum hydroxide, bonding, high strength, high temperature resistance, but easy to dry caking, should not be put for a long time, the skin has a certain corrosive.
Fused alumina zirconia refractory cement for intermediate frequency
Fused alumina zirconia refractory cement is casting of AZS clinker as refractory aggregate.The ingredients of the fused alumina zirconia refractory cement (mass%) are ZrO2 30, Al2O3 48, SiO2 20,Phase is a -al2o3,Mullite baddeleyite, glass phase,Maximum particle size is 5mm.When in use, only need to add water mixing, the volume density is 3.2g/cm3, porosity is 12%, the porosity of weak precipitation, under the temperature of 1400 DEG C to glass corrosion resistant performance is strong, also can be used as a sealing layer and a mud slurry.
Low shrinkage Zircon refractory cement
Low shrinkage Zircon refractory cement is the introduction of a certain amount of chromium containing material in AZS basic composition, volume density of >2.9g/cm3, reheat shrinkage (1400 DEG C, 3H <0.2%),The corrosion resistance of glass liquid is superior to the above two kinds of ramming material, as long as the water is added, it can also be used as sealing layer and pouring material-refractory cement.
Taurus Refractory ramming mass Factory mainly engaged in professional manufacturer of development, production and sales of the refractory mixture such as melting copper, aluminum and zinc furnace lining. And supply castable refractory for copper smelting, ramming mass for molten copper,fire clay,refractory mortar, refractory cement ,refractory mixture, refractory concrete and silica sand for copper smelting.
Website: http://www.jnrefractory.com
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
Email: info@jnrefractory.com
gyjinniu@163.com
products list : castable refractory cement for up lead copper rod Molten Zinc Refractory Casting Molten Zinc Ramming Mass Molten Aluminum Refractory Material refractory castable for up lead copper rod Special Refractory Ramming Mass Copper alloy refractory materials for electric furnace acidic refractory for electric furnace body electric furnace refractory material for copper smelting Corrosion resistance Molen Zinc Refractory Castable for up lead copper rod High Strength Refractory Mortar Refractory installation services Fireclay Light-weight Castable Refractory Casting Refractory Accessory Refractory Material Corrosion resistance Quartz sand High Grade Composite Silica Ramming Mass Corundum Plastic Refrctory Alumina Composite Ramming Mass for horizontal continuous casting Silica Refractory Ramming Mass for horizontal continuou casting quartz sand refractory for copper smelting silica sand refractory for core induction furnace refractory concrete block pre-cast refractory block refractory ramming mixture fire clay for up lead copper rod refractory mortar for non core induction furnace refractory cement for copper smelting high grade composite silica mortar silica refractory cement Magnesia refractory cement
Zircon refractory cement for intermediate frequency of composition (mass%) was ZrO2 62, SiO2 32, Al2O3 2, Fe2O3 0.5, Bulk density is greater than 3g/cm3,The fire resistance is about 1790, Maximum particle size 0.5mm.Zircon refractory cement binding agent for phosphate two aluminum hydroxide, bonding, high strength, high temperature resistance, but easy to dry caking, should not be put for a long time, the skin has a certain corrosive.
Fused alumina zirconia refractory cement for intermediate frequency
Fused alumina zirconia refractory cement is casting of AZS clinker as refractory aggregate.The ingredients of the fused alumina zirconia refractory cement (mass%) are ZrO2 30, Al2O3 48, SiO2 20,Phase is a -al2o3,Mullite baddeleyite, glass phase,Maximum particle size is 5mm.When in use, only need to add water mixing, the volume density is 3.2g/cm3, porosity is 12%, the porosity of weak precipitation, under the temperature of 1400 DEG C to glass corrosion resistant performance is strong, also can be used as a sealing layer and a mud slurry.
Low shrinkage Zircon refractory cement
Low shrinkage Zircon refractory cement is the introduction of a certain amount of chromium containing material in AZS basic composition, volume density of >2.9g/cm3, reheat shrinkage (1400 DEG C, 3H <0.2%),The corrosion resistance of glass liquid is superior to the above two kinds of ramming material, as long as the water is added, it can also be used as sealing layer and pouring material-refractory cement.
Taurus Refractory ramming mass Factory mainly engaged in professional manufacturer of development, production and sales of the refractory mixture such as melting copper, aluminum and zinc furnace lining. And supply castable refractory for copper smelting, ramming mass for molten copper,fire clay,refractory mortar, refractory cement ,refractory mixture, refractory concrete and silica sand for copper smelting.
Website: http://www.jnrefractory.com
Contact: Mr. Niu
Tel: +86-371-64372566
Fax: +86-371-64372588
Mobile Phone: +86-15137151612
Email: info@jnrefractory.com
gyjinniu@163.com
products list : castable refractory cement for up lead copper rod Molten Zinc Refractory Casting Molten Zinc Ramming Mass Molten Aluminum Refractory Material refractory castable for up lead copper rod Special Refractory Ramming Mass Copper alloy refractory materials for electric furnace acidic refractory for electric furnace body electric furnace refractory material for copper smelting Corrosion resistance Molen Zinc Refractory Castable for up lead copper rod High Strength Refractory Mortar Refractory installation services Fireclay Light-weight Castable Refractory Casting Refractory Accessory Refractory Material Corrosion resistance Quartz sand High Grade Composite Silica Ramming Mass Corundum Plastic Refrctory Alumina Composite Ramming Mass for horizontal continuous casting Silica Refractory Ramming Mass for horizontal continuou casting quartz sand refractory for copper smelting silica sand refractory for core induction furnace refractory concrete block pre-cast refractory block refractory ramming mixture fire clay for up lead copper rod refractory mortar for non core induction furnace refractory cement for copper smelting high grade composite silica mortar silica refractory cement Magnesia refractory cement